Nowadays, the increase in population and the rapid depletion of nonrenewable energy sources brings the need for energy. In this case, scientists are forced to develop technologies by using renewable energy sources. Sun is the unlimited and renewable energy source. Organic solar cells absorb the light from the sun by the active polymer layer and transform it into electrical power. Organic solar cells are advantageous than inorganic ones because of being low-cost, easy-to-use and proper for large scale applications. In this project, it is aimed to produce organic solar cells by using specific amounts of carbon nanotube (CNT) doping. According to this aim, it is detected by using the fluorescence spectroscopy that CNTs can be used in organic solar cells. Later, the homogenous distribution of doping SWCNT into donor material was displayed by AFM, and correct proportion of SWCNTs are chosen by those images. In order to increase the efficiency of organic solar cell SWCNT doped P3HT was used as donor molecule. The acceptor molecule was PCBM in here. Surface characterization of prepared samples was made by Atomic Force Microscope (AFM), while electrical characterization of them is done with airless environment cabin (glove-box) system in nitrogen environment. As a result, devices prepared with addition of cyclohexanone in P3HT: SWCNT%:PCBM new load paths to carbon nanotubes were provided, as a result of the measurements short circuit current obtained was raised from the reference to 53%. The best yields were found as 2.24% in 0.2% SWCNT doped devices. This result shows efficiency is healed according to the reference rate as 64%. In this study, certain amounts of carbon nanotube doped organic solar cells were produced, which are highly efficient rather than traditional organic solar cells and low cost, easy-to-produce rather than inorganic solar cells, by using environmentally friendly materials.