When adding 2% or 4% sodium polyacrylate as habit modifier, standard milky-white octahedral NaCl crystals grew gradually in saturated NaCl solution on the bottom of the container. [1] [2] Sodium polyacrylate is well known as a highly water-absorbable polymer with many carboxylate anions. In the case of low concentration (0.01%, 0.02%, 0.05%, 0.1% and 0.5%) sodium polyacrylate many small or microscopic crystals whose shapes were nearly octahedrons and had {111} faces were observed with an optical microscope on the bottoms of the solution containers. In low concentration sodium polyacrylate, octahedral NaCl crystals made up of electrostatically unstable {111} faces grew similarly to crystals in high concentrations of 2% or 4% NaCl. Therefore, by adding sodium polyacrylate to saturated NaCl solution, cleaved rock salt crystals in this sol were observed to find out whether or not a change in crystal morphology from cuboids of {100} faces to octahedrons of {111} faces would occur. Regardless of the sodium polyacrylate concentrations of 0.01%, 0.02%, 0.05%, 0.1%, 0.5% and 2%, all cuboid crystals changed into a pyramidal shape in which four of the side surfaces formed an equilateral triangle. When one side of each equilateral triangle face was rotated so the square face of the crystal was soaked in the NaCl sol, all crystals grew into octahedrons of high transparency. Sodium polyacrylate, even under a low concentration, caused morphological change in the NaCl crystals. Many carboxylate anions in the sodium polyacrylate attracted sodium ions and the repulsive force between the carboxylate anions became weak, excluding the water in the internal space of the polymer. We considered that the stabilizing {111} faces of gathered sodium ions attached to carboxylate anions. Chloride and sodium ions coordinated continuously to minimize the NaCl surface area, growing into an octahedral and lowering the surface energy of the NaCl crystal. [3]