Peanut Hull as an Antioxidant in Metal Coats

科展類別
臺灣國際科展
屆次
2006年
科別
化學科
得獎情形
未得獎作品
學校名稱
Philippine Science High School-Main Campus
指導老師
CARIDAD G. GICARAYA
作者
ROBERT GLEN R. ABESAMIS

摘要或動機

A study was done to determine if the antioxidants found in peanut hulls could be used\r
for lessening the corrosion rate of iron. Peanut hulls were ground then divided into two\r
batches, P1 and P2, then oven-dried at temperatures of 50°C and 60°C, respectively. The\r
moisture content of each batch was then determined before performing methanolic extraction\r
to isolate the antioxidants. Eighteen iron strips of approximately the same surface areas were\r
thoroughly cleaned and weighed, then divided into six groups. The iron strips in the first five\r
groups were respectively coated with pure extract from batch P1; a 1:1 mixture of P1 extract\r
and turpentine; pure P2 extract; a 1:1 mixture of P2 extract and turpentine; and pure\r
turpentine. No treatment was done on the sixth group. All iron strips were exposed to air to\r
allow formation of rust thru atmospheric corrosion. After 12 days, the iron strip were cleaned\r
and weighed; then the individual corrosion rates of the metals were determined.\r
The corrosion rates of the metals treated with pure P1 extract, the P1-Turpentine, and\r
the P2-Turpentine mixtures were found to be significantly lower than the corrosion rates of\r
the metals without treatment, at 5% level of significance in a t-Test for independent samples.\r
The average corrosion rates of all the treated metals were found to be lower than that of\r
metals treated with pure turpentine, though not significantly. The corrosion rate of the metals\r
coated with turpentine was not significantly less than that of untreated metals. The corrosion\r
rates of the metals were also found not to be dependent with the moisture as there was no\r
significant difference in the mean corrosion rates of metals treated with P1 extract and those\r
treated with P2 extract, with or without turpentine.\r
The project has shown that peanut hull extracts can be used to lessen the production\r
of rust on the surface of the metal. Moisture content of the hulls was not found to be a factor\r
in lessening the corrosion rate.