IF鋼在鹽酸溶液中之腐蝕速度隨鹽酸濃度之增加而增加。12M之硝酸溶液對IF鋼具最強腐蝕性，而最低(0.1M)及最高(16M)濃度之硝酸溶液對IF鋼之腐蝕性則相對較弱。硫酸對IF鋼之腐蝕速度則由低濃度至高濃度呈現極大變化，當硫酸濃度由0.1M漸增至3M時腐蝕速度亦隨之增加，爾後腐蝕速率減小，至硫酸濃度由8M時反而呈現極大之重量增加。由於表面腐蝕層不適於XRD分析，故由EDS結合FTIR分析得知H?SO?/8M-24hrs.情況下試片表面之腐蝕層為Fe?O?。由SEM觀察發現腐蝕速率較大之條件，如HCI/12M-1min.及HNO?/12M-1min.處理過後，試片表面甚至出現具晶體對稱性之蝕恐。由本研究之初步成果發現：是溫下可以利用中等濃度(如8M)之硫酸液來處理鋼鐵，使之表面生成一緻密之氧化鐵(Fe?O?)，達到防蝕之效果。IF (interstitials free) steel was processed in various aqueous acid solutions to observe the corrosion behavior. The corrosion rate of IF steel in HCI(aq) increases with the concentration of HCI(aq). HNO?(aq) with concentration of 12M was observed to be the most aggressive for IF steel. The corrosion rate of IF steel in H?SO? solution increases from 0.1M to 3M and then decreases gradually with the concentration. A large amount of weight gain even observed when the concentration was 8M. The protective layer produced during H?SO?/8M-24hurs. treatment was analyzed to be Fe?O? by using SEM (Scanning Electron Microscope), EDS (Energy Dispersive Spectroscopy) and FTIR (Fourier Transform infrared). Etch pits with crystallographic symmetry were observed on the specimens treated with conditions HCI/12M-imin. and HNO?/12M-1min. Processing condition H?SO?/8M-24hrs. could be employed in corrosion prevention for IF steel under ambient environment.
「為配合國家發展委員會「推動ODF-CNS15251為政府為文件標準格式實施計畫」，以及 提供使用者有文書軟體選擇的權利，本館檔案下載部分文件將公布ODF開放文件格式， 免費開源軟體可至LibreOffice 下載安裝使用，或依貴慣用的軟體開啟文件。」